CPC A61K 6/818 (2020.01) [A61C 5/77 (2017.02); A61C 7/14 (2013.01); A61C 8/0013 (2013.01); A61K 6/20 (2020.01); A61K 6/58 (2020.01); C04B 41/5038 (2013.01); C04B 41/87 (2013.01); A61C 13/083 (2013.01); C04B 2111/00836 (2013.01); C04B 2237/348 (2013.01)] | 13 Claims |
1. A dental product comprising:
a base material formed of a zirconia sintered body; and
a porcelain layer formed by sintering porcelain,
wherein the porcelain comprises ceramic, glass, or glass-ceramic, and comprises 65.0 to 90.0 mol % of SiO2, 4.0 to 15.0 mol % of Al2O3, 0.1 to 10.0 mol % of Na2O, 1.0 to 10.0 mol % of K2O, and 0.01 to 15.0 mol % of CaO, and optionally less than 0.1 mol % of Li2O based on total 100 mol % of constituent components. and has a suitable firing temperature of 1050° C. or more, and the porcelain layer has a fracture toughness value of 1.20 MPa·m0.5 or more.
|