CPC C01B 32/198 (2017.08) [C01B 32/23 (2017.08); C01B 2204/04 (2013.01); C01P 2004/20 (2013.01)] | 18 Claims |
1. A method for the manufacture of graphene oxide from kish graphite comprising:
A. providing kish graphite;
B. pre-treating the kish graphite comprising the following successive sub-steps:
i. a sieving step wherein the kish graphite is classified by size as follows:
a) Kish graphite having a size below 50 μm,
b) Kish graphite having a size greater than or equal to 50 μm,
the fraction a) of kish graphite having a size below 50 μm being removed;
ii. a flotation step with the fraction b) of kish graphite having a size above or equal to 50 μm;
iii. an acid leaching step wherein an acid is added so that a ratio in weight (acid amount)/(kish graphite amount) is between 0.25 and 1.0; and
iv. optionally, the kish graphite is washed and dried; and
C. an oxidation step of the pre-treated kish graphite obtained after step B) in order to obtain graphene oxide.
|